Subramanian, B. and Ashok, K. and Subramanian, K. and Sastikumar, D. and Selvan, G. and Jayachandran, M. (2009) Evaluation of corrosion and wear resistance titanium nitride (TiN) coated on mild steel (MS) with brush plated nickel interlayer. Surface Engineering, 25 (7). pp. 490-495. ISSN 0267-0844

[img] PDF
Restricted to Registered users only

Download (400Kb) | Request a copy

Abstract

Titanium nitride (TiN) coatings were deposited onmild steel (MS) by direct current reactivemagnetron sputtering. With the aim of improving the corrosion resistance of TiN, an additional nickel interlayer was brush plated on the steel substrates before TiN film formation. The phases have been identified with X-ray diffraction analysis. The hardness values of TiN layers were found to increase with the increase in thickness of the Ni interlayer. The wear track investigations of TiN layers showed that the TiN/MS system was worn out by abrasive wear mechanism while on the film with Ni interlayer is by adhesive wear. It was found that the TiN/Ni/MS stack had a weaker tendency towards corrosion and higher corrosion resistance in 3?5%NaCl than the bare MS substrate, Ni/MS and TiN/MS specimen.

Item Type: Article
Uncontrolled Keywords: Titanium nitride; Magnetron sputtering; Hard coatings; Corrosion resistance
Subjects: Electrochemical Materials Science
Divisions: UNSPECIFIED
Depositing User: ttbdu cecri
Date Deposited: 02 Apr 2012 05:07
Last Modified: 02 Apr 2012 05:07
URI: http://cecri.csircentral.net/id/eprint/1200

Actions (login required)

View Item View Item